For our esteemed clients, we offer a distinguished assortment of Zinc Chromate Yellow Primer. The offered range is processed and verified under the inspection of our adroit professionals employing premium grade chemical compounds in sync with the set industrial standards. Extensively used in various places for painting, these products are highly demanded in the market for their indispensable features.
Features:
Quick drying
Chemical resistance
Premium quality
Specifications:
Scope | An anticorrosive primer for metal protection with chemical resistance and rust inhibitive property due to chromate pigments. |
Type | Single Pack, Air Drying |
Composition | Zinc Chromate pigmented alkyd based primer. |
Application | By brush or Spray |
Theoretical Coverage | 16 M2/ Ltr at 25 microns dry film thickness (DFT) |
Dry Film Thickness | 25-30 microns |
% Volume Solid | 40 ± 2% |
Drying Time | Surface Dry – 1 Hour |
Recoatability Time | 18 Hours |
Flash Point | Not below 30° C |
Colour | Greenish Yellow |
Shelf Life | 1 year in tight sealed condition |
Finish |
|
Additional Information:
Treading ahead with an objective to meet diversified demands of our valued clients, we are offering a wide array of superior quality Epoxy Zinc Chromate Primer. These products are processed under the guidance of experienced professionals, using optimum quality chemical compounds. In order to eliminate any type of flaw, our quality controllers check the entire gamut against standardized quality parameters.
Features:
Withstand water immersion
Outstanding rust inhibitive property
Unmatched quality
Specifications:
| Scope | A good anticorrosive primer for metal protection, coupled with excellent chemical resistance of the medium with outstanding rust inhibitive property of the chromate pigments. It is a good base coat for epoxy finishes and largely employed n chemical environments and corrosive atmosphere. It is suitable for structures under splash of water and alcohols. With suitable top coat it can withstand water immersion as well. Also, recommended for floating roof of tanks under marine conditions. |
| Type Composition | Two pack. Cold cured. |
| Composition | Zinc Chromate pigmented Polyamide adduct cured Epoxy Resin. |
| Temperature Resistance | 120° C dry heat |
| Application | By brush or Airless spray |
| Theoretical Coverage | 16 M2/ Ltr at 25 microns DFT 10 M2/ Ltr at 40 microns DFT |
| Pot Life | 8 hours when mixed |
| Mixing Ratio | Base to Hardner 4:1 by volume (30 minutes maturing after mixing should be done prior to application) |
| Dry Film Thickness | 25 – 40 microns |
| % Volume Solid | 40 ± 2% |
| Drying Time | Touch Dry – 1 Hour Hard Dry – 16 Hours Full Cure – 7 Days |
| Recoatability Time | 18 Hours |
| Flash Point | Not below 20°C |
| Colour | Greenish Yellow |
| Package | 20 Liters |
| Finish | Matt |
| Surface Preparation | If blasting is not practical, manual cleaning to Sa 2 Standard should be done |
| Overcoating | Recommended with Epilac Enamels, Coal Tar Epoxy or Poly Urethane Paints & Chloro Rubber Paints |